Properties\Materials	evoHIPS	evoABS	HS ABS	HS ASA	Aramid ABS	Aramid ASA	ASA CF10	Generic ABS*
Density in g/cm^3	1,05	1,05	1,04	1,07	1,05	1,07	1,10	1,05
Tensile Strength at Yield in MPa	16	45	39	42	35	40	exp. ~85	40
Tensile Elongation at Break	50%	>10%	13%	>35%	6%	6&	1,80%	11%
Flexural Modulus in MPa	2000	2450	2000	1900	2350	2200	7580	1805
Izod Impact Strength (23°C) in kJ/m^2	90	33	19	43,5	---	---	---	20,5
Izod Impact Strength (-30°C) in kJ/m^2	---	16	10	6	---	---	---	---
Charpy Impact Strength, Unnotched, in kJ/m^2	7	---	---	---	14	25	16,8	23
Charpy Impact Strength, Notched, in kJ/m^2	---	---	---	---	6,1	7,5	5,4	4
Heat Deflection Temperature in °C	88	93	87	86	88/75	89/79	101/95	82
Vicat Softening Temperature in °C	87	93	95	94	95	94	---	---

*The Generic ABS is an average calculated out of three well known and used offers from other manufacturers

Properties\Materials	LWPA	LWPA GF30	LWPA CF15	HTPA	HTPA CF15	HTPA GS10	HTPA FR V0 Ceramic	Generic PA*
Density in g/cm^3	1,18	1,34	1,18	1,14	1,25	1,01	1,49	1,14
Tensile Strength in MPa	50	55	90	80	170	87	55	75
Tensile Elongation at Break	2%	>3%	4%	4%	2%	2,7%	1,20%	3%
Flexural Modulus in MPa	2900	4500	8000	3300	15000	4200	6000	3125
Charpy Impact Strength, Unnotched, in kJ/m^2	139	25	60	135	47	26	---	58
Charpy Impact Strength, Notched, in kJ/m^2	6,8	4	4	---	---	---	---	---
Heat Deflection Temperature in °C	60	180/65	180/65	120/90	200	120/90	120/90	85

*The Generic PA is an average calculated out of three well known and used offers from other manufacturers

Properties\Materials	BasicCOP	eCOP	DuroCOP	COP ToughM	COP 95A	LF COP	COP FR V0	COP CF10	Generic PETG*
Density in g/cm^3	1,27	1,23	1,18	1,35	1,13	1,32	1,26	1,32	1,27
Tensile Strength in MPa	48	59	64	45	22	40	40	45	39
Tensile Elongation at Break	58%	400% / 4% Yield	210% / 7% Yield	3%	400% / 38% Yield	>100% / 4% Yield	40%	5%	48%
Flexural Modulus in MPa	1950	2000	1575	3150	150	1850	2350	4250	2050
Izod Impact Strength (23°C) in kJ/m^2	126	101	---		---	---	---	---	85
Izod Impact Strength (-30°C) in kJ/m^2	57	---	---		40 (at -40°C)	---	---	---	---
Charpy Impact Strength, Unnotched, in kJ/m^2	---	---	No break	85	---	No Break	---	17	---
Charpy Impact Strength, Notched, in kJ/m^2	---	---	86	4	---	6	3	5,4	---
Heat Deflection Temperature in °C	70	70	100	80/70	Vicat 170°C	Vicat 70°C	63/58	80	68

*The Generic PETG is an average calculated out of three well known and used offers from other manufacturers

Properties\Materials	evoGreen FormX	PPS	PCTG	PCTG GF10	PCTG CF10	LF PC	PET CF15
Density in g/cm^3	1,30	1,33	1,23	1,31	1,28	1,32	1,40
Tensile Strength in MPa	65	65	46	55	70	55	130
Tensile Elongation at Break	0,5%	2%	220% / 4% Yield	8%	5%	8%	2,5%
Flexural Modulus in MPa	12500	3650	1600	exp. ~4500	exp. ~7500	2200	9000
Izod Impact Strength (23°C) in kJ/m^2	---	---	93	45	48	---	---
Izod Impact Strength (-30°C) in kJ/m^2	---	---	---	---	---	---	---
Charpy Impact Strength, Unnotched, in kJ/m^2	55	18	---	---	---	50	40
Charpy Impact Strength, Notched, in kJ/m^2	8	1,3	---	---	---	12	---
Heat Deflection Temperature in °C	60	129/107 Vicat 236°C	76/64	78/68	78/68	140/130	125